Study of Chromium Effect on Structure and Wear-Resisting Properties of Complex Alloyed Brass
1 UMMC, 1 Uspenskiy Ave., Verkhnaya Pyshma, Sverdlovsk Region, 624091, Russian Federation
2 PJSC “RZ OCM”, 1 Kombinatskaya Str., Revda, Sverdlovsk Region, 623280, Russian Federation
3 Ural Federal University, 19 Mira Str., Ekaterinburg, 620002, Russian Federation
* Corresponding author: firstname.lastname@example.org
The microstructure of CuZnMnAlSiNiCr complex alloyed brass was examined. The effect of various chromium content in the range from 0.00 to 0.33 wt.% on the composition and morphology of intermetallic compounds was established, and the amount of chromium-based intermetallic compounds was estimated. Microhardness of intermetallic compounds of various morphology was determined. The effect of chromium content on wear rate of brass samples was estimated. The range of chromium content at which samples wear rate is minimal was estimated.
© The Authors, published by EDP Sciences, 2021
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.