Mechanical properties of sulphate reduction bacteria on the durability of concrete in chloride condition
1 Jamilus Research Centre for Sustainable Construction (JRC), Faculty of Civil and Environmental Engineering, Universiti Tun Hussein Onn, Malaysia
2 Micro Pollutant Research Centre (MPRC), Faculty of Civil and Environmental Engineering, Universiti Tun Hussein Onn, Malaysia
* Corresponding author: teddy_bhagas@yahoo.com
In construction, concrete durability is an important material globally used in engineering, material of which can be applied in the fields of specialized marine construction. The ingress of chloride into concrete causes deterioration in the concrete due to the reinforcement corrosion. Adding bacteria into concrete can improve material properties and increase durability with mechanism resist chloride ingressed in the concrete . Ingress of Chloride into the concrete of bacteria is particularly suited for applications of chloride ion penetration in concrete. The objective of the research is to determine the effect of adding bacteria into the concrete properties. The bacteria used in this research is locally isolated and enriched to the suite with the concrete environment. The type of the bacteria used is identified as Sulphate Reduction Bacteria (SRB). The SRB added into the concrete mix with concentrations of 3%, 5% and 7%. Whereas, concentration of bacteria water of cement is 0.5. The mechanical properties test conducted with 28th, 56th, 90th, 180th and 360th day of curing period. The test was using cyclic wetting and drying to study the exposure to chloride condition, such as compressive strength, tensile strength and flexural test. Cubes in the size of 150 mm × 150 mm × 150 mm were prepared for compressive strength test and cylinder 150 mm × 300 mm were prepared for the tensile strength test. The flexural strength test was on the prism in the size of 100 mm × 100 mm × 500 mm. The result of compressive strength test shows, that gave significant strength of 66.3 MPa on the 360th day. The tensile strength and flexural strength have a similar trend as compressive strength results, where both results were optimum . The tensile strength test shows that 4.52 MPa tends to control 3.96 MPa. The result of flexural strength test was 8.23 MPa for compared to control of 5.99 MPa. The overall results of the bacteria indicate promising outcome and further study on chloride condition capability is encouraging.
© The Authors, published by EDP Sciences, 2019
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.