Microstructure and Properties of Low Cost TC4 Titanium Alloy Plate
1 Baoti Group Ltd., Baoji 721014, China
2 Baoji Titanium Industry Co., Ltd., Baoji 721014, China
* Corresponding author: firstname.lastname@example.org
The changing law of microstructure and mechanical properties of low cost TC4 titanium alloy during deformation and annealing was investigated. The results show that the coarse cast dendritic structure of slab is broken to form rod-like or equiaxial α+β transformed microstructure by rolling deformation. After annealing, the microstructure of plate becomes uniform, moreover, the flake secondary α separates out and the amount of primary α phase decreases with the increase of annealing temperature and gradually tends to equiaxization. The tensile strength and ductility of plate show an increased tendency with deforming. When annealing temperature increases, the tensile strength firstly increases, and then reaches the maximum value at 820 °C, after that, it gradually decreases. The yield strength and reduction of area show decreasing trend as a whole, but the elongation has a little change. The plate has preferable matching of strength and ductile after annealing treatment at 750~820 °C for 1h in air.
© The Authors, published by EDP Sciences, 2016
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.