Growth of AlGaN Film on Si (111) Substrate
1 Institute of Laser Engineering, Beijing University of Technology, Beijing 100022, China
2 Guangdong redsolarphotovoltaic technology Co., LTD zhongshan 528437, Guangdong, China
At present, the applications of AlxGa1−xN are extensive, such as for visible-blind ultraviolet detectors, laser diodes, light emitting diodes (LEDs) and HEMTs. In this paper, Al0.25Ga0.75N and Al0.32Ga0.68N films have been grown on 2 in Si (iii) substrates by MOCVD. The low-temperature (6 K) photoluminescence (PL) spectrum and XRD rocking curve measurements have been employed to study the crystal quality of samples, and the phonon replica peak can be observed, which indicate that the samples have better quality in a small-localized region. The surface morphology of samples was investigated by AFM and the result of wavy surface agrees with the deduction from XRD rocking curve measurements. The sheet resistance mappings have been shown, and it indicates the nonuniformity of AlGaN film on Si (iii) will increase sharply as the Al content increases.
© Owned by the authors, published by EDP Sciences, 2016
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.