A study of microstructure and tensile property with casting S45C welding
Department of industrial education, National Taiwan Normal University, Taipei City, 10610, Taiwan
2 Department of Mechanical and Automation Engineering, Chung Chou University of Science and Technology, Yuanlin City, 51022, Changhua County, Taiwa
Corresponding author : email@example.com
For energy saving and longer life time of a large casting iron may use of weld repairs or make up to more save manufacture time and energy than re-casting. Such as breakage, crack and wear in large casting iron castings used weld to repair casting for eco-energy.
The purpose of this study is to investigate the dissimilar joint property of S45C carbon steel with the multi-layer method and the multi-pass welding method. Four weld rods, experimentally examined the influence on microstructures, which were marked as A, B, C and D, respectively. The microstructures of joint bead were observed by the optical microscope. The specimens of tensile test were made according to ASTM E8M. The experimental results were shown as following:
1. The pearlite structures and the bainite structures were formed in welded zone by the weld rod of middle carbon steels. The yield strength and ultimate strength of the specimens were 360MPa and 460MPa.
2. The feature of welded specimen was close to stainless steel due to the stainless steel rod included some Cr and Ni. In addition, a ferritic-austenitic two-phase stainless steel was observed in optical microscope.
© The Authors, published by EDP Sciences, 2018
This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.