Caracterization and Compressive Strength of Biocomposite Hydroxyapatite-Borosilicate with Hight Temperature Sintering
1 Department of Mechanical Engineering, Bung Hatta University, Padang Indonesia
2 Department of Chemistry, Andalas University, Padang Indonesia
3 Department of Mechanical Engineering, Andalas University Padang Indonesia
* Corresponding author: firstname.lastname@example.org
The use of Hydroxyapatite as bone graft material continues to increase. To utilize hydroxyapatite, it is often formed into biocomposite. The formation of hydroxyapatite biocomposite intended to address the fragile hydroxyapatite weaknesses. The added element in the formation of this biocomposite is borosilicate. Mixing of this material is arranged with certain composition using ball miling. To form a test specimen, it was printed with compacting force of 5 KN, 15 KN and 25 KN. Test results Compressive Strength.and XRD showed that addition of borosilicate did not change the compound that is hydroxyapatite, but the intensity of hydroxyapatite tends to decrease with addition of borosilicate amount, this is corroborated by FTIR testing. For visible compressive strength, the maximum value occurs at 75: 25 compositions, ie 45 MPa, 42.9 MPa and 52.3 MPa. This suggests that the addition of borosilicate in biocomposite formation does not alter hydroxyapatite compound and can generally increase the compressive strength and modulus of elasticity to 25% wt% borosilicate addition.
© The Authors, published by EDP Sciences, 2018
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.