Microstructure and wear behavior of austempered high carbon high silicon steel
Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka, Surathkal, Mangaluru 575025, India.
* Corresponding author: firstname.lastname@example.org
In the present investigation, the influence of austempering temperature and time on the microstructure and dry sliding wear behavior of high silicon steel was studied. The test specimens were initially austenitised at 900°C for 30 minutes, thereafter austempered at various temperatures 280°C, 360°C and 400°C, for varying duration from 30 to 120 minutes. These samples after austempering heat treatment were subsequently air cooled to room temperature, to generate typical ausferritic microstructures and then correlated with the wear property. The test outcomes demonstrate the slight increase in specific wear rate with increase in both austempering temperature and time. Specific wear rate was found to be minimum at an austempering temperature of 280°C, that exhibits lower bainite microstructure with high hardness, on the other hand specific wear rate was found to be slightly high at increased austempering temperatures at 360°C and 400°C, due to the upper bainite structure that offered lower hardness to the matrix. The sample austempered at 280°C for 30 minutes offered superior wear resistance when compared to other austempering conditions, mainly due to the presence of fine acicular bainitic ferrite along with stabilized retained austenite and also some martensite in the microstructure.
© The Authors, published by EDP Sciences, 2018
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. (http://creativecommons.org/licenses/by/4.0/).
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.