Forming and quenching behaviours in hot stamping of thin quenchable sheets
Toyohashi University of Technology, Department of Mechanical Engineering, 1-1 Hibarigaoka, Tenpaku, Toyohashi, Aichi, Japan
a Corresponding author: e-mail: firstname.lastname@example.org
A thin aluminium-coated quenchable steel sheet was hot-stamped to investigate the effect of the thickness. The sheets having 0.6, 1.0 and 1.6 mm in thickness were heated at 900 ∘C by a furnace and formed after 7 s from the furnace. The cooling rates of 0.6 mm and 1.0 mm in thickness from 900 ∘C to 400 ∘C under air cooling were 20.9 ∘C/s and 13.6 ∘C/s, respectively. The hardness of the air-cooled sheets having 1.0 mm in thickness was 300 HV1, whereas that of the sheet having 0.6 mm in thickness was 380 HV1 because of the high cooling rate. The Vickers hardness of the U-bent sheets of 0.6 and 1.0 mm after 7 s from the furnace without the holding time at the bottom dead centre were 500 and 430 HV1, respectively.
© Owned by the authors, published by EDP Sciences, 2015
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.