Study of Recrystallization Kinetics of 1565ch Aluminum Alloy during hot deformation
1 Samara National Research University, 443086 Samara, Russia
2 JSC ”Arconic SMZ”, 443051 Samara, Russia Study is funded by a grant of the Russian Science Foundation, project 18-79-10099.
* Corresponding author: email@example.com
The present study addresses recrystallization process in Al-Mg-Mn-Zn-Zr system alloy samples. The samples are collected from cast ingot, produced by casting to industrial DC mold, and homogenized based on standard industrial practice. After that the samples were rolled with different hot rolling schedules. Rolled samples were annealed at different temperatures and their resultant microstructure was examined using optical microscope. During the study new grains nuclei generation rate and their growth rate were determined, analytical records, describing recrystallization kinetics, were obtained, main differences, specific to this alloy recrystallization in 350 ºС-450 ºС temperature range, were identified.
© The Authors, published by EDP Sciences, 2020
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.