Polyamide 12/E-glass Fabric Composite Production with Dip-coating
Yildiz Technical University, Department of Metallurgical and Materials Engineering,
34220,
Esenler, Istanbul,
Turkey
* Corresponding author: aylinaltinbay@gmail.com
In this study PA12 was reinforced with E-glass woven fabric by dip-coating. PA12 powder and ethanol suspensions were prepared with ratios at 30, 40 and 50% of powder to obtain different fibre contents. Coated fabrics were laid-up and kept in oven at 60°C to evaporate ethanol. Then it was placed in a compression mould and pressed. Obtained laminates were subjected to tensile, bending and impact tests. Fractured surfaces were observed. It was found that mechanical properties were highest when 40% PA powder used in suspension with dip-coating with additional lamination. Fibre failure and fibre pull-out were observed on fractured surfaces.
© The Authors, published by EDP Sciences, 2018
This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.