The Effect of Temperature Curing on Geopolymer Concrete
1 Department of Civil Engineering, Faculty of Civil Engineering and Planning ITS Surabaya, Indonesia, 60111
2 Konsorsium Riset Geopolimer Indonesia (KORIGI), Lab Beton dan Bahan Bangunan ITS, Surabaya, Indonesia
* Corresponding author: email@example.com
This study presents curing temperature influences to behaviors of geopolymer concrete. The concrete was fly ash based, with the ratio of fly ash to alkaline activator was 65%:35%. Ratio coarse aggregate to fine aggregate was 60%:40%, ratios Na2SiO3/NaOH were 1.5:2 and 2.5. A polycarboxilate superplasticizer with ratio was 2% to fly ash weight. Form of the test specimens were cylinder with diameter of 10 cm and 20 cm high. Steam curing conducted were at 40°C, 60°C and 80°C for 24 hours. The control specimens were treated at normal moist curing. Tests conducted were compressive strength, tensile strength, porosity and elasticity modulus. The results indicated that at the elevated temperature the compressive strength increases as well as tensile strength but decreases the closed porosity of specimens. The elasticity modulus had a similar tendency.
© The Authors, published by EDP Sciences, 2017
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.