Synthesis and Characterization of Co/Ni/CoNi-ZSM-5 Catalyst for Hydrogen Production

¹ Department of Chemical Engineering, Faculty of Engineering, Diponegoro University, Semarang
² Laboratory of Material Technology, Centre of Research and Service Diponegoro University, Semarang
³ Department of Mechanical Engineering, Faculty of Engineering, Diponegoro University, Semarang

^* Corresponding author: widayat@live.undip.ac.id

Abstract

Nickel is commonly used as a catalyst in hydrogen production. However, the use of nickel catalysts in the steam reforming process has the disadvantage of coke formation and high cost. Therefore, in this research, Ni/ZSM-5 catalyst synthesis was used to reduce production cost and an addition of cobalt (Co) metal to avoid coke formation. The method consists of a synthesis of ZSM-5 catalyst using hydrothermal process. Furthermore, the crystalline product was impregnated with the metal cobalt, nickel and combination of cobalt-nickel as much as 2% by weight metal/weight of the catalyst. Then the XRD and EDX characterization of Co/ZSM-5, Ni/ZSM-5, and CoNi/ZSM-5 was done followed by catalytic testing in the production of hydrogen from glycerol using steam reforming process. From XRD characterization results showed that Co/ZSM-5 catalyst has a crystallinity of 78.69%, Ni/ZSM-5 catalyst has 70.04% crystallinity and CoNi/ZSM-5 catalyst has 76.99% crystallinity. Catalytic testing on hydrogen production showed that CoNi/ZSM-5 catalyst produced the highest hydrogen concentration of 1,756.33 ppm while Ni/ZSM-5 catalyst produces 1,240 ppm and Co/ZSM-5 catalyst produces 491 ppm.