Jnhmicro-texture of AZ31 Magnesium Alloy in Situ Tracking During Compressing Deformation
1 School of Material Science & Engineering, Shenyang Ligong University, Shenyang 110159 China
2 Shenyang Institute of Technology, Liaoning, Fushun 113122, China
Micro-texture evolvement mechanism of AZ31 magnesium alloy during compressing deformation had been studied in situ tracking method by EBSD(Electron backscatter diffraction). The micro-texture at same observation areas, which compressed three times continually at different deformation degree, had been investigated. The results presented that the micro-texture of AZ31 magnesium alloy rolling state is typical (0001) basic texture. When deformation degree was 11% and the temperature was 170ଌ, grains orientation changed remarkably, and most grains had been twined fully and little grains twined partially. The initial basical rolling texture weakened gradually, and twined grains tropism accorded with and 86.3° orientation.
© The Authors, published by EDP Sciences, 2016
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.